Tungsten Carbide Hardness Range
04-13-2010, 08:25 AM,
Tungsten Carbide Hardness Range
Dear Fellows:

I would like to know what is your tungsten carbide (WC + 17%Co) macrohardness (rockwell) range? Mine is around 91HRC in average. The reason to ask is to check if I could make it higher so to achieve better CpK reading under GE requirement. Smile

Or you could share with me how to to increase it...

Thank you
04-14-2010, 11:57 AM,
RE: Tungsten Carbide Hardness Range
Is it HRN?

HRC is used under HRC70.

04-14-2010, 06:50 PM,
RE: Tungsten Carbide Hardness Range
Usually in thermal spray applications, they use to measure MACROHARDNESS, that is only as reference value, only to have an idea of the hardness of the coating, and this value for Wc17%Co is about 65 to 72 HRc, it depend of the system or parameters been used, to obtain this values you must use an HVOF system
To determine Microhardness value, that is quite the real hardness value of the coating, HR15N is used and this value for Wc__Co coatings can be around 90, some times is used Hv0.3, so Rockwell is used for Macrohardness measures and Vickers is used for microhardness .
Best regards
04-14-2010, 08:23 PM,
RE: Tungsten Carbide Hardness Range
Hi Ykang

HRC (Rockwell C scale) is not a suitable test for these coatings. Some quote HRC values as a guide because many are more familiar with scale. To do so requires conversion/equivalents from a practical test method. In the case of tungsten carbide coatings HRC equivalents are very hit and miss and meaningless. As said by Luigi, it seems 91 seems to be a realistic value for HR15N Rockwell superficial scale, but not HRC.

If you are considering increasing hardness, you need to be cautious. Harder WC /17%Co coatings are not necessarily better coatings Sad Harder coatings can sometimes be the result of matrix hardening as a posed to increased density. This tends to be detrimental to the coating reducing ductility and abrasive wear resistance. I think there are some threads on the forum that discuss this in more detail.

Your hardness checking procedure may well be a factor in improving your CpK reading under GE requirement.
04-16-2010, 01:55 AM,
RE: Tungsten Carbide Hardness Range
Dear All:

My mistake...It should be 91HR15N..Not HRC...Smile

Possibly Related Threads…
Thread Author Replies Views Last Post
  Request for solution to reduce porosity in HVOF Tungsten Carbide Coatings sreenuvundela 7 9,415 07-22-2020, 08:01 AM
Last Post: Simon Kim
  Tungsten Carbide HVOF Removal PrecisionCarbide 9 9,902 02-24-2020, 11:17 AM
Last Post: Packiaraj Mutharasu
  roller surface high roughness Tungsten carbide coating Ra 0.15-0.3mm zhuminkun 6 2,829 02-08-2019, 04:59 AM
Last Post: Taz
  Dark surface after grinding of plasma tungsten carbide coating Lazha 1 2,372 05-31-2017, 12:07 PM
Last Post: loriolo
  HVAF tungsten carbide to replace hard chrome - Help??!!! Adamreis 2 2,650 02-20-2017, 11:04 PM
Last Post: Vig
  Effective Way of Testing hardness of Tungsten Carbide MANGESH 2 5,168 12-03-2015, 09:25 PM
Last Post: alaskangrown
  Tungsten Carbide coatings Sealants sorousheti 5 5,443 11-23-2015, 10:18 AM
Last Post: sorousheti
  Cold Spray with Tungsten Carbide LLBHW 3 10,876 04-24-2015, 01:06 AM
Last Post: Fermit
  HVOF Tungsten Carbide - New Line Setup David 1 3,762 08-16-2014, 03:51 PM
Last Post: Gordon
  Tungsten Carbide HVOF Coated Ball Valves grinding and Lapping constraints --- Reg sreenuvundela 4 9,584 07-29-2013, 09:04 AM
Last Post: Met.Eng.
  pencil hardness and tukon hardness test transit 6 16,813 10-04-2012, 02:15 PM
Last Post: bruisjem
  Tungsten Carbide coating Guna 1 5,223 05-25-2010, 07:54 PM
Last Post: Gordon
  Tungsten Carbide Microfinish engineerraj 12 12,769 07-17-2009, 12:52 PM
Last Post: karunanidhi
  Tungsten Carbide HVOF Removing. Kiroga 2 9,009 12-04-2008, 04:03 PM
Last Post: Pete_F
  Tungsten carbide coating problem ycwbycwb 8 13,619 05-20-2008, 01:42 PM
Last Post: ycwbycwb

Users browsing this thread: 1 Guest(s)

Surface Engineering Forum Sponsor - Alphatek Hyperformance Coatings Ltd