Each pass thickness & interpass temp. confused
07-19-2020, 03:20 PM,
#41
RE: Each pass thickness & interpass temp. confused
Dear DMan,
Coatings made of stainless steel (Diamalloy 1003 or 316 L) cannot be used as a bond coat. Conversely, these layers will accelerate corrosion of the substrate in a humid atmosphere.
Regards
Vadim
Reply
07-19-2020, 04:17 PM,
#42
RE: Each pass thickness & interpass temp. confused

Hi Vadim

Any possibility that a thin ss layer of Diamalloy be applied on MS base ..then apply a bond coat followed by top coat.

Just a guess...since you tell we can't use it as a bond coat.

I was just wondering since I thought this SS layer (Diamalloy) may prevent the MS base from corroding.

correct me ,I may be absolutely wrong here.

Warm regards
DMAN

Dear DMan,
Coatings made of stainless steel (Diamalloy 1003 or 316 L) cannot be used as a bond coat. Conversely, these layers will accelerate corrosion of the substrate in a humid atmosphere.
Regards
Vadim
[/quote]

Reply




Possibly Related Threads…
Thread Author Replies Views Last Post
  interpass temperature macleod-s 1 781 08-11-2019, 04:15 PM
Last Post: velocity
  High Temp Adhesive for TSA Adhesion test wrjordan 3 5,820 07-22-2011, 06:51 PM
Last Post: MichiganMan
  high temp during hvof coating ehsan 6 10,787 07-05-2011, 03:25 PM
Last Post: Justin
  How to pass the acid test? jurongwei 10 10,374 10-17-2009, 05:27 PM
Last Post: Gordon
  Jet Kote water inlet temp... Intel55 4 5,956 03-19-2009, 10:53 PM
Last Post: Gordon



Users browsing this thread: 1 Guest(s)





Surface Engineering Forum Sponsor - Alphatek Hyperformance Coatings Ltd