RE: AISI 420 powder
Thanks Stephen
Strange how 13Cr steels are widely used in wire form but not powder.
|
|
01-31-2008, 05:57 AM,
|
|
Stephen Booth
SuperMember
|
Posts: 268
Threads: 22
Joined: Dec 2007
Reputation:
11
| |
RE: AISI 420 powder
Yes, I am sure it is demand driven. The applications for coating with HVOF or even Laser, or PTA 420 are in my opinion slightly old solutions, basically "grandfathered" into the customers procedure. However, as a jobs shop, if I can provide the solution with the specified coating, and inform of a modern replacement material, then I have some advantages over the competition. Most manufacturers do have a 431SS in the product range, which is rather similar to the 420...
|
|
05-02-2008, 04:45 AM,
|
|
Binson
Newbie
|
Posts: 1
Threads: 0
Joined: May 2008
Reputation:
0
| |
RE: AISI 420 powder
Stephen Booth Wrote:Hi looking for some sources for the following
1. HVOF 420
Powder needed AISI 420 stainless with factory certification, with mesh size suitable for use with Diamond Jet 2700 using Propane. If you have parameters would be nice as well.
Small Quantity: This is a new application, but maybe small about 50 kg on first order, thereafter maybe up to 150 kg per year.
Dear Stephen,
I have an experience using AISI 420 powder by our HVOF TAFA JP5000, it was quite difficult bdoninf after spray finished, occured crack but after recoating twice we were succed. We have exceed powder material about 2 jars if you interested to buy. please let me know.
2. We also use AISI 420 on regular basis for Plasma Welding, quantity used is about 250 kg per year, mesh size is -150/+45.
|
|
05-02-2008, 08:00 PM,
|
|
Gordon
Administrator
|
Posts: 1,802
Threads: 70
Joined: Jun 2006
Reputation:
9
| |
RE: AISI 420 powder
Hi Binson
to the Surface Engineering Forum.
|
|
|