Posted by Gordon England on January 08, 2004 at 03:40:56:
In Reply to: Pull Off Adhesion strength of Shot and Grit Blasted metallizing posted by sandeep on January 01, 2004 at 10:35:03:
: Dear Sir
: WISH U A HAPPY NEW YEAR..........
: 01.
: What would be the approximate pull off adhesion strength (psi) value of thermal spray metallizing (Zn) for surface prepared by Shot and Grits to Sa 2.5 grade.
: 02
: Whether Coarser grits give better pull off adhesion strength against finer grits.
: 03
: What would be the pull off adhesion strength of thermal spray metallizing if surface is prepared by MS or Chilled Cast Iron Grits.Chilled iron grits may cause rapid wear and tear to blasting facilities. Can we recommend MS Grits for LPG cylinder surface preparation.
: Regards
: Sandeep
01. Many specifications call for around 600 or 800 psi as a minimum tensile bond strength for flame spray zinc coatings. It is difficult to give a more precise answer as there are too many factors in addition to the differences in test methods (most commonly accepted methods ASTM D4541 and ASTM C633). Also be aware that coatings in excess of about 0.020" thickness need to be tested to reduce the effect of adhesive absorption interfering with the results. I can only predict that shot blasting will produce lower bond strengths than grit blasting. You will need to conduct test for your particular set-up.
02. I have found in some cases that finer grit blast finishes provide higher tensile bond strengths, but this probably will not apply to shear strength.
03. The problem using soft grits is that they will very quickly blunt and act in a peening action as opposed to grit blasting action.
Hope this helps
Regards Gordon
Follow Ups:
Surface Engineering Forum
Surface Engineering Message Board Archive
Surface Engineering Message Board Archive Index
www.gordonengland.co.uk
Introducing
Nature of Thermal Spray Coatings
Surface Engineering in a Nutshell
Surface Engineering Forum
Thermal Spray Gun Repair Service
Plasma Consumable Parts
Thermal Spray Powder Supplies
Applications:
Thermal Spray Coatings on Carbon and Glass Fibre Reinforced Polymers
HVOF Coating of Paper Making Roll
Abradable Coatings
Thermal Spray Processes:
Combustion Wire Thermal Spray Process
Combustion Powder Thermal Spray Process
Arc Wire Thermal Spray Process
Plasma Thermal Spray Process
HVOF Thermal Spray Process
HVAF Thermal Spray Process
Detonation Thermal Spray Process
Plasma Flame Theory
Cold Spray Coating Process
Wear and Use of Thermal Spray Coatings
Corrosion and Use of Thermal Spray Coatings
Glossary of Thermal Spray and Surface Engineering Terms
Image Directory for Thermal Spray Coatings
Plasma Gas Flow Information
Plasma Gas Flow Correction Calculator
Contact Form
Links to other interesting sites related to thermal spray and surface engineering
Reciprocal Links
Periodic Table of the Elements
SI Units
Calculators for Conversion between Units of Measurement
Hardness Testing
Surface Engineering Message Board Archive
Surface Engineering Message Board Archive Index
Photography Gallery2
Photography Gallery3
© Copyright Gordon England