Tungsten Carbide coatings Sealants
10-28-2015, 11:41 AM,
#1
Tungsten Carbide coatings Sealants
Hi All
Does anyone have experience in sealing Tungsten Carbide coatings by slurry?
Is this a common method?
If anyone have article in this field, please send for me.
Thank you
sorousheti@yahoo.com Wink Wink
Reply
10-29-2015, 04:29 PM,
#2
RE: Tungsten Carbide coatings Sealants
Hi Sorousheti
The selection of the different kind of sealer, depend on their specific working properties, pore sizes, working temperature
resistance to chemicals media, and climatic conditions, so the choice of the sealer will be done for each case, a slurry usually is applied when there is high temperature, but tungsten carbide has low temperature limit (about 600 °C), when the work piece will be in high temperature (about 900°C) is better to use Chrome carbide coatings, for more information about sealer see: Dichtol, Loctite, Amerlock, Aremco, Munari System, etc.
Best regards
Luigi
Reply
11-02-2015, 08:41 AM,
#3
RE: Tungsten Carbide coatings Sealants
Thank you Luigi
That's right.... but I hear about sealants that applyed in slurry form, then heated in low temperature (about 200 C) and eliminate pore and increase strength. this sealants use for chrome plating and thermal spray coatings.
I want some information about this sealants.
Reply
11-08-2015, 08:37 PM,
#4
RE: Tungsten Carbide coatings Sealants
Hi Sorousheti
this kind of sealant are ceramic slurry so you must contact Aremco (https://www.aremco.com), but there isn't any sealant that can increase the coating strenght, only eliminate porosity and protect the piece agains corrosion.
Best regards
Luigi
Reply
11-17-2015, 12:50 PM,
#5
RE: Tungsten Carbide coatings Sealants
Hi sorousheti,

In a proper sprayed wccocr coating <1% porosity, I cannot image any sealer would penetrate that as it would even take a few days for water to penetrate!

br,
Joris
Reply
11-23-2015, 10:18 AM,
#6
RE: Tungsten Carbide coatings Sealants
Hi dear Joris
Yes you right... this ceramic sealers use for fill porosity in chrome plating and WCCo coatings <1% porosity but it use for increase in wear resistant for tungsten carbide coatings.
Reply




Possibly Related Threads…
Thread Author Replies Views Last Post
  Tungsten Carbide Microfinish engineerraj 15 16,633 02-17-2023, 09:41 PM
Last Post: J!m
Photo Pitting in HVOF Tungsten Carbide mrobie 4 2,249 08-31-2022, 02:08 PM
Last Post: Red Baron
  Epoxy Sealants for Ceramic Chromium Oxide DMan 0 1,365 06-27-2021, 11:39 AM
Last Post: DMan
  Request for solution to reduce porosity in HVOF Tungsten Carbide Coatings sreenuvundela 7 12,267 07-22-2020, 08:01 AM
Last Post: Simon Kim
  Tungsten Carbide HVOF Removal PrecisionCarbide 9 14,104 02-24-2020, 11:17 AM
Last Post: Packiaraj Mutharasu
  roller surface high roughness Tungsten carbide coating Ra 0.15-0.3mm zhuminkun 6 5,068 02-08-2019, 04:59 AM
Last Post: Taz
  Dark surface after grinding of plasma tungsten carbide coating Lazha 1 3,737 05-31-2017, 12:07 PM
Last Post: loriolo
  HVAF tungsten carbide to replace hard chrome - Help??!!! Adamreis 2 4,114 02-20-2017, 11:04 PM
Last Post: Vig
  Effective Way of Testing hardness of Tungsten Carbide MANGESH 2 7,354 12-03-2015, 09:25 PM
Last Post: alaskangrown
  Cold Spray with Tungsten Carbide LLBHW 3 12,654 04-24-2015, 01:06 AM
Last Post: Fermit
  HVOF Tungsten Carbide - New Line Setup David 1 4,989 08-16-2014, 03:51 PM
Last Post: Gordon
  Tungsten Carbide HVOF Coated Ball Valves grinding and Lapping constraints --- Reg sreenuvundela 4 11,389 07-29-2013, 09:04 AM
Last Post: Met.Eng.
  Buffer or build up layers under HVOF Carbide Coatings Stephen Booth 12 18,876 05-19-2011, 11:00 PM
Last Post: Met.Eng.
  Tungsten Carbide coating Guna 1 6,553 05-25-2010, 07:54 PM
Last Post: Gordon
  Tungsten Carbide Hardness Range ykang 4 48,218 04-16-2010, 01:55 AM
Last Post: ykang



Users browsing this thread: 1 Guest(s)





Surface Engineering Forum Sponsor - Alphatek Hyperformance Coatings Ltd