RE: Renew plasma after heat treatement
For me, I work on repair manual and serviceable or repairable limits, after heat treatment, we normally will re-inspect on the coating and see if there is visual chippings, flake off..debond..etc, if it iswithin the limit, we will try to protect the coating to continue for other repair.
Ofcourse that is based on our application and the parts we work on. Focusing on customer need, if the repair can be minimized, or reduced workscope, it means cost saving for the customers =)
regards,
alexangel1226
|