Crack indication Stellite 1 HVOF
01-15-2019, 03:40 AM,
#1
Crack indication Stellite 1 HVOF
Hello guys

Help me please Sad
i have case that my stellite 1 HVOF spray already done with thickness 180 - 270 microns. But my customer want to do red dye penetrant testing in coating spray. This is the 1st time i do red dye penetrant testing in coating spray.
i attach photo, my penetrant testing in to coated part result

   

i wanna ask, is this method (red dye penetrant testing) is suitable to spray coating ??
and
how to do correct method spray to prevent this coating cracks.

FYI
powder Stellite 1 Durametal HVOF
HVOF DJ 2600 (hydrogen)
Hybrid gun

Thank you so much
regards
Reply
02-12-2019, 12:58 PM,
#2
RE: Crack indication Stellite 1 HVOF
(01-15-2019, 03:40 AM)achmadarifudinh Wrote: Hello guys

Help me please Sad
i have case that my stellite 1 HVOF spray already done with thickness 180 - 270 microns. But my customer want to do red dye penetrant testing in coating spray. This is the 1st time i do red dye penetrant testing in coating spray.
i attach photo, my penetrant testing in to coated part result



i wanna ask, is this method (red dye penetrant testing) is suitable to spray coating ??
and
how to do correct method spray to prevent this coating cracks.

FYI
powder Stellite 1 Durametal HVOF
HVOF DJ 2600 (hydrogen)
Hybrid gun

Thank you so much
regards

Suitable or not cracks are real and penetration test doesn' t cause that.
My question is about geometry. Is it a kind of blade or is the other side of coating has also coating?
Edges are heating faster then thick area and cooling rate may cause this. Are you preheating tool? Cooling with air or slowly?
Reply
02-12-2019, 09:52 PM,
#3
RE: Crack indication Stellite 1 HVOF
Hi Achmadarifudinh

I thing ur problem is cooling. You can try this method

Preheat 100-120 C
Apply 50 micron bond coat (arcspray is best way i thing )
And than spray top coat. Preheating is important!!! Ur first top coat lyres have to confort heated surface.

Good luck Smile
Reply
02-20-2019, 01:48 AM,
#4
RE: Crack indication Stellite 1 HVOF
(02-12-2019, 12:58 PM)velocity Wrote:
(01-15-2019, 03:40 AM)achmadarifudinh Wrote: Hello guys

Help me please Sad
i have case that my stellite 1 HVOF spray already done with thickness 180

Suitable or not cracks are real and penetration test doesn' t cause that.
My question is about geometry. Is it a kind of blade or is the other side of coating has also coating?
Edges are heating faster then thick area and cooling rate may cause this. Are you preheating tool? Cooling with air or slowly?

Thank you for ur reply sir.
It's kind of blade in leading area section. i coated 25 cm from tip blade with 2cm width. that's true leading edge have curve geometry.
am already do preheating to 100-120 celcius as ASM 5A reference.
is it meaning for cooling air is cooling air in side coated blade when blade is spraying ??
or cooling air when blade after coated ??

Thanks
Regards
Achmad
Reply
02-20-2019, 03:13 AM,
#5
RE: Crack indication Stellite 1 HVOF
my thoughts:
try to maintain the preheat, and keep the heat during the spraying, and allow for slow cooling, I would suiggest even a bit higher on the temperature even to 200C but not going over 250C, and slow cool in Vermeculite
Reply
07-07-2021, 07:19 AM,
#6
RE: Crack indication Stellite 1 HVOF
as of 2021 are there any formal OEM or Certification standards (ISO or API or similar) for the inspection of HVOF WC coatings using dye penetrant.

customers often asking for this type of NDT, but my stance is Dye Penetrant on HVOF coatings is not a valid test:

any one have any formal documentation on this?
Reply




Possibly Related Threads…
Thread Author Replies Views Last Post
  Stellite 31 Daneizer 0 1,598 02-05-2021, 04:15 PM
Last Post: Daneizer
  Parameter Stellite 6 HVOF DJ2600 achmadarifudinh 0 2,637 12-07-2018, 01:36 AM
Last Post: achmadarifudinh
  grinding wheel for stellite 6 hvof coating raviswanadha 8 17,993 12-07-2018, 01:15 AM
Last Post: achmadarifudinh
  Stellite 6 welding rods Desmond 7 16,996 04-18-2016, 07:31 AM
Last Post: sreenuvundela
  Can stellite 6 fuse ??? Met.Eng. 1 5,244 03-12-2014, 06:19 AM
Last Post: sreenuvundela
  Crack on WC/Co Met.Eng. 1 4,380 07-18-2013, 12:40 AM
Last Post: Alberto Villalobos
  Chromium Carbide crack novakmichal86 4 7,667 03-01-2013, 09:04 AM
Last Post: kschewe
  Stellite Powder test guru2707 1 7,901 02-27-2013, 08:05 AM
Last Post: novakmichal86
  Stellite Hardfacing test guru2707 4 14,114 06-04-2012, 01:03 PM
Last Post: Aseem
  Laser Cladding Stellite#6 Kedarnath 6 19,634 02-04-2011, 01:51 PM
Last Post: Nick4u1
  stellite coating samsarani 1 11,264 07-29-2010, 09:19 PM
Last Post: djewell
  Crack line ykang 18 21,378 04-18-2009, 11:24 PM
Last Post: LEN WOOD
  crack in NiCr Panf 11 12,878 10-22-2008, 10:56 AM
Last Post: Panf
  crack in WC/Co Panf 8 15,669 07-14-2007, 04:58 PM
Last Post: fhyuan
  linear indication simonlee 5 15,051 09-14-2006, 05:42 AM
Last Post: simonlee



Users browsing this thread: 1 Guest(s)





Surface Engineering Forum Sponsor - Alphatek Hyperformance Coatings Ltd