01-15-2019, 03:40 AM,
#1
Crack indication Stellite 1 HVOF
Hello guys

Help me please Sad
i have case that my stellite 1 HVOF spray already done with thickness 180 - 270 microns. But my customer want to do red dye penetrant testing in coating spray. This is the 1st time i do red dye penetrant testing in coating spray.
i attach photo, my penetrant testing in to coated part result

   

i wanna ask, is this method (red dye penetrant testing) is suitable to spray coating ??
and
how to do correct method spray to prevent this coating cracks.

FYI
powder Stellite 1 Durametal HVOF
HVOF DJ 2600 (hydrogen)
Hybrid gun

Thank you so much
regards
Reply
02-12-2019, 12:58 PM,
#2
RE: Crack indication Stellite 1 HVOF
(01-15-2019, 03:40 AM)achmadarifudinh Wrote: Hello guys

Help me please Sad
i have case that my stellite 1 HVOF spray already done with thickness 180 - 270 microns. But my customer want to do red dye penetrant testing in coating spray. This is the 1st time i do red dye penetrant testing in coating spray.
i attach photo, my penetrant testing in to coated part result



i wanna ask, is this method (red dye penetrant testing) is suitable to spray coating ??
and
how to do correct method spray to prevent this coating cracks.

FYI
powder Stellite 1 Durametal HVOF
HVOF DJ 2600 (hydrogen)
Hybrid gun

Thank you so much
regards

Suitable or not cracks are real and penetration test doesn' t cause that.
My question is about geometry. Is it a kind of blade or is the other side of coating has also coating?
Edges are heating faster then thick area and cooling rate may cause this. Are you preheating tool? Cooling with air or slowly?
Reply
02-12-2019, 09:52 PM,
#3
RE: Crack indication Stellite 1 HVOF
Hi Achmadarifudinh

I thing ur problem is cooling. You can try this method

Preheat 100-120 C
Apply 50 micron bond coat (arcspray is best way i thing )
And than spray top coat. Preheating is important!!! Ur first top coat lyres have to confort heated surface.

Good luck Smile
Reply
02-20-2019, 01:48 AM,
#4
RE: Crack indication Stellite 1 HVOF
(02-12-2019, 12:58 PM)velocity Wrote:
(01-15-2019, 03:40 AM)achmadarifudinh Wrote: Hello guys

Help me please Sad
i have case that my stellite 1 HVOF spray already done with thickness 180

Suitable or not cracks are real and penetration test doesn' t cause that.
My question is about geometry. Is it a kind of blade or is the other side of coating has also coating?
Edges are heating faster then thick area and cooling rate may cause this. Are you preheating tool? Cooling with air or slowly?

Thank you for ur reply sir.
It's kind of blade in leading area section. i coated 25 cm from tip blade with 2cm width. that's true leading edge have curve geometry.
am already do preheating to 100-120 celcius as ASM 5A reference.
is it meaning for cooling air is cooling air in side coated blade when blade is spraying ??
or cooling air when blade after coated ??

Thanks
Regards
Achmad
Reply
02-20-2019, 03:13 AM,
#5
RE: Crack indication Stellite 1 HVOF
my thoughts:
try to maintain the preheat, and keep the heat during the spraying, and allow for slow cooling, I would suiggest even a bit higher on the temperature even to 200C but not going over 250C, and slow cool in Vermeculite
Stephen James Booth
www.ipsteknokraft.com
www.teknokraft.com
Indonesia WhatsApp +6281905603262

Reply




Possibly Related Threads…
Thread Author Replies Views Last Post
  Stellite 31 Daneizer 0 392 02-05-2021, 04:15 PM
Last Post: Daneizer
  Parameter Stellite 6 HVOF DJ2600 achmadarifudinh 0 1,350 12-07-2018, 01:36 AM
Last Post: achmadarifudinh
  grinding wheel for stellite 6 hvof coating raviswanadha 8 14,600 12-07-2018, 01:15 AM
Last Post: achmadarifudinh
  Can stellite 6 fuse ??? Met.Eng. 1 3,970 03-12-2014, 06:19 AM
Last Post: sreenuvundela
  Crack on WC/Co Met.Eng. 1 3,331 07-18-2013, 12:40 AM
Last Post: Alberto Villalobos
  Chromium Carbide crack novakmichal86 4 5,982 03-01-2013, 09:04 AM
Last Post: kschewe
  stellite coating samsarani 1 9,809 07-29-2010, 09:19 PM
Last Post: djewell
  Crack line ykang 18 18,537 04-18-2009, 11:24 PM
Last Post: LEN WOOD
  crack in NiCr Panf 11 10,552 10-22-2008, 10:56 AM
Last Post: Panf
  crack in WC/Co Panf 8 13,630 07-14-2007, 04:58 PM
Last Post: fhyuan
  linear indication simonlee 5 12,131 09-14-2006, 05:42 AM
Last Post: simonlee



Users browsing this thread: 1 Guest(s)





Surface Engineering Forum Sponsor - Alphatek Hyperformance Coatings Ltd