Matrix cohesion problem of WC CoCr
02-22-2018, 02:08 AM, (This post was last modified: 02-22-2018, 03:17 AM by bsjkiller.)
#1
Matrix cohesion problem of WC CoCr
Coating parameter

1. Spray machine : Orelikon mecto DJ 2700
2. Gas flow
⓵ Oxygen : 40FMR / 150psi
⓶ FUEL(LPG) : 36FMR / 105psi
⓷ Air : 47FMR/ 105psi
3. Stand off : 230 mm
4. Powder feed rate : 40 g/min
5. Gun traverse speed : 100 cm/min
6. Test piece hold : Φ220
7. Test piece hold RPM : 490 RPM
8. Powder : WOKA3652 (WC10Co4Cr)
9. Test poece size : 15mm * 12mm * 4mm

Q: Coating conditions of sample 1 and sample2 are the same.
But the results(matrix cohesion) are different.
what is the reason?

Sample1
[Image: bsjkiller10kg1small.jpg] Load 10kg

[Image: bsjkiller20kg2small.jpg] Load 20kg

[Image: bsjkiller1kg3small.jpg] Load 1kg

Sample 2

[Image: bsjkiller10kg4small.jpg] Load 10kg

[Image: bsjkiller20kg5small.jpg] Load 20kg

[Image: bsjkiller1kg6small.jpg] Load 1kg
Reply




Possibly Related Threads…
Thread Author Replies Views Last Post
Video Problem WC CoCr Lyokha ibn Ivanovich 2 1,246 05-24-2020, 06:13 AM
Last Post: Lyokha ibn Ivanovich
  Matrix cohesion problem of WC CoCr sams5313 2 1,175 09-22-2019, 04:34 PM
Last Post: loriolo
  Repairing of delaminated areas of a WC-CoCr coating avalarezo 1 1,438 03-12-2018, 08:33 PM
Last Post: Vig
  Coatings for Polymer Matrix Composites Nadiir 6 5,067 03-30-2014, 08:38 AM
Last Post: Nadiir
  Oxide and porosity in WC-CoCr coating ycwbycwb 4 10,778 05-10-2008, 02:39 PM
Last Post: Gordon
  Carbide in Chromium-Nickel matrix mechanical properties KRYM2006 8 11,335 07-03-2007, 05:09 PM
Last Post: Gordon



Users browsing this thread: 1 Guest(s)





Surface Engineering Forum Sponsor - Alphatek Hyperformance Coatings Ltd