HVOF T800 Tensile Bond Strength issue
03-03-2015, 09:36 AM, (This post was last modified: 03-04-2015, 06:44 AM by wgg237.)
#1
HVOF T800 Tensile Bond Strength issue
Hi guys,

We are developing HVOF T800 with JP8000 (kerosene/O2). Currently, we just got a good coating microstructure(porosity, oxides, unmelted good), but faced a low TBS issue (Only Avg.~5000psi, far away from the target value 8500 psi. Cohesive failure in coating), as well as micro hardness of coating (Avg. 640 HV0.3, low than target value: 675). We had pre heating prior to coat spraying.

Appreciate your good ideas & experiences to share, Thanks!
Reply
03-03-2015, 11:03 AM,
#2
RE: HVOF T800 Tensile Bond Strength issue
(03-03-2015, 09:36 AM)wgg237 Wrote: Hi guys,

We are developing HVOF T800 with JP8000 (kerosene/O2). Currently, we just got a good coating microstructure(porosity, oxides, unmelted good), but faced a low TBS issue (Only Avg.~5000psi, far away from the target value 8500 psi. Cohesive failure in coating), as well as micro hardness of coating (Avg. 640 HV0.3, low than target value: 675). We had pre heating prior to coat spraying.

Appreciate your good ideas & experiences to share, Thanks!

Attached is metallographic photo of coating at 200X...

Hi,

When heating the substrate it may be oxidized and it reduces adhesion. Furthermore, you monolayer thickness is approximately 10 micrometers - a very much. Then thicker a monolayer, the higher the residual stresses in the coating and thus lower bond strength with the substrate. Try to increase the speed of movement of the workpiece surface (RPM) twice, at 5 micrometers thickness of the monolayer reduced stress significantly.

Regards
Reply
03-05-2015, 01:52 AM,
#3
RE: HVOF T800 Tensile Bond Strength issue
(03-03-2015, 11:03 AM)Vadim Verlotski Wrote:
(03-03-2015, 09:36 AM)wgg237 Wrote: Hi guys,

We are developing HVOF T800 with JP8000 (kerosene/O2). Currently, we just got a good coating microstructure(porosity, oxides, unmelted good), but faced a low TBS issue (Only Avg.~5000psi, far away from the target value 8500 psi. Cohesive failure in coating), as well as micro hardness of coating (Avg. 640 HV0.3, low than target value: 675). We had pre heating prior to coat spraying.

Appreciate your good ideas & experiences to share, Thanks!

Attached is metallographic photo of coating at 200X...

Hi,

When heating the substrate it may be oxidized and it reduces adhesion. Furthermore, you monolayer thickness is approximately 10 micrometers - a very much. Then thicker a monolayer, the higher the residual stresses in the coating and thus lower bond strength with the substrate. Try to increase the speed of movement of the workpiece surface (RPM) twice, at 5 micrometers thickness of the monolayer reduced stress significantly.

Regards

Thanks for your guidance... It seems more reasonable... Will let you know the tends after get the trial result.
Reply
09-11-2023, 09:18 AM,
#4
RE: HVOF T800 Tensile Bond Strength issue
Dear all

I have the same problem recently (same equipment and coating requirement)
I tried decrease the deposit rate to 0.0002"/ pass with increase the linear speed but still fail.
And it's found that compare to higher deposit rate (0.0050"/ pass), lower rate seems no significant improvement and inconsistent with theory.
Is it possible that the problem is caused equipment ? (leak, powder feed type, etc...) (The device was recently calibrated.)
We use 3-way splitter to feed to gun with 1 powder feeder, will it affect the consistency of powder feeding ?

Thank you
Reply




Possibly Related Threads…
Thread Author Replies Views Last Post
Pencil Ball Mill Shaft- Journal Bearing Area HVOF Coating Issue tobjung 0 745 02-02-2023, 06:44 PM
Last Post: tobjung
  Spark Issue on DJ2600 HVOF Flame xxxxmgulkokan 3 2,135 08-31-2022, 03:15 PM
Last Post: Red Baron
  metco 101bns powder / tensile strength RogerMilam 6 6,040 05-08-2022, 07:53 PM
Last Post: landemarre
  Metallic HVOF bond coat to TBC APS top coat Gas turbines achmadarifudinh 0 1,839 07-08-2019, 08:34 AM
Last Post: achmadarifudinh
  T800 parameter Ping Cheng 2 3,438 03-14-2019, 09:56 AM
Last Post: Ping Cheng
  304SS and 420Ss Arc Spray as bond layer for HVOF velocity 1 2,403 07-06-2018, 08:38 PM
Last Post: sprayloud
  Info needed on Bond Strength for Thermal Spray powders hereticgame 1 3,330 10-10-2017, 11:39 AM
Last Post: Vadim Verlotski
  Tensile Test TBC giuiori75 1 3,399 09-29-2017, 02:35 AM
Last Post: achmadarifudinh
  HVOF JK parameters for T800 plyer 8 13,914 07-27-2017, 01:41 PM
Last Post: technovel
  tensile test failure analysis (HELP) CHI3 0 2,830 05-23-2017, 08:07 PM
Last Post: CHI3
  T800 coating delamination alvliew 5 5,694 05-05-2017, 02:54 AM
Last Post: KevinS
  95Ni 5Al bond strength alaskangrown 1 3,847 01-15-2016, 05:09 PM
Last Post: loriolo
  Qualifying T800 to F50TF45 Class A mmgerrie 4 6,528 12-23-2015, 03:38 AM
Last Post: alvliew
  HVOF DJ2600 DJ8W powder feeder issue vetrinit 5 8,416 06-17-2015, 04:39 PM
Last Post: loriolo
Shocked Hard Crome Plating Bond strength Met.Eng. 4 7,842 02-24-2015, 02:37 AM
Last Post: Simon Kim



Users browsing this thread: 1 Guest(s)





Surface Engineering Forum Sponsor - Alphatek Hyperformance Coatings Ltd