Hi,
We are working on feed crushing blade coating. We applied hot coating WC/Co+NiCrBSi %50 but not get enough service life. I saw some brazing application and an electro spark surface coating machine.
It's name is Rocklinizer. It works on 3 different electrode. TitaniumCarbide, TungstenCarbide.
Is any body try to use this machine?
Is any body know the bonding strength ?
What is the correct application this like surface parts? (Feed crushing blade, crushing hammer, farming blades ect)
I check some doc. about this machine. I thing may be work well on this like application.
Thanks for your reply.