Coating hardness conversion
12-19-2006, 05:32 PM,
#1
Coating hardness conversion
Dear Colleagues, note my query:
TS-coating hardnesses are expressed in several ways. Our friends over-there, the AM-people are usually telling us the hardness as HRC. We EU-people favour HV 0,3 or at least some Vickers.
How to convert HRC to HV concerning sprayed coatings at least to get a rough figure. If one uses the tables and calculators found on the net, one gets a too low figure for HV, compared to actual hardness measurements.
It seems if one adds 5 to 10 points to the HRC-scale, the outcome in HV touches actual HV-figures.
Does anyone have a somewhat "reliable" compensation solution to this.
All this only because I'm nowadays, after 40 yrs in the TS-business, entertaining myself by technical translations crosswise between FIN-ENG-SWE.
Br Bhe[/font][/size]
Reply
12-27-2006, 04:25 PM,
#2
RE: Coating hardness conversion
Hi bhellman

Sign0016 to the Surface Engineering forum.

Unless you do a direct comparison between the different hardness tests for your particular coating, then I would definitely say no to any "reliable" generic conversion solution. HRC (Rockwell C) is often quoted for thermal spray coatings mainly because people can relate to or visualise this hardness scale better than say Rockwell Superficial HR15N or Vickers. Problem is that the hardness of the majority of thermal spray coatings can not be practically measured using HRC. Most HRC values stated are from generic conversion tables, which are at best rough guides, and in many cases are impossible to confirm by testing when used with TSCs. I think it is a very bad practice to quote HRC values (unless actually tested by this method) without indicating the original hardness test method and values as well.
Reply
12-28-2006, 09:20 AM,
#3
RE: Coating hardness conversion
Gordon Wrote:Hi bhellman

:sign0016: to the Surface Engineering forum.

Unless you do a direct comparison between the different hardness tests for your particular coating, then I would definitely say no to any "reliable" generic conversion solution. HRC (Rockwell C) is often quoted for thermal spray coatings mainly because people can relate to or visualise this hardness scale better than say Rockwell Superficial HR15N or Vickers. Problem is that the hardness of the majority of thermal spray coatings can not be practically measured using HRC. Most HRC values stated are from generic conversion tables, which are at best rough guides, and in many cases are impossible to confirm by testing when used with TSCs. I think it is a very bad practice to quote HRC values (unless actually tested by this method) without indicating the original hardness test method and values as well.

Thank you Gordon.
Actually I'm aware of this dilemma. My aim is to find some way to express the HV hardness region for TSCs when some HRC value is known. This to provide some idea to people, not too deeply familiar with TS. For self-fluxing fused coatings I presume that standard conversion tables can be used. But when talking about high quality oxide ceramics and hardmetals, the std. tables give too low values. These coatings can usually be found in the area of 1000 HV +- 250 HV. Maybe a rough honest expression could be 750 - 1250 HV, for instance?
br bhe
Reply
12-28-2006, 03:22 PM,
#4
RE: Coating hardness conversion
Hi bhellman



When you can actually do HRC tests on coatings say like a fused NiCrBSi or a thick 13%Cr steel, then at least you can do cross reference tests to see if conversion tables are reasonable or not. With very hard coatings like oxide ceramics and cermets usually HRC tests are not possible. Come to think of it, I wouldn't use HRC for these in the bulk form either. I can remember someone trying to test a sintered tungsten carbide part (~1700 HV) on an HRC machine only to succeed in chipping the diamond indenter and breaking his test part in half.

I have done a lot of work with hard coatings and measuring cross-section microhardness (HV0.3) and HR15N surface hardness (coatings in excess of 0.012" or 300 micrometre thick). From memory I will show roughly the relationship between HV/0.3 and HR15N and the corresponding conversion to HRC. Please note that it is not possible to verify the HRC conversion because the actual HRC test is not viable on these coatings and to be honest think that expressing the hardness for these types of material in HRC is a bit pointless and can be misleading.

Plasma sprayed chromium oxide
1800 HV/0.3 96.5 HR15N (79-80 HRC converted)
1500 HV/0.3 95.5 - 96 HR15N (75-76 HRC converted)

Chromium oxide, alumina and WC/Co
1250 HV/0.3 94.5 - 95 HR15N (71-72 HRC converted)
800 -1000 HV/0.3 92 - 94 HR15N (65-70 HRC converted)

Generally as a rough guide (range relative to grade and quality)
Chromium oxide coatings 1000 - 1800 HV (92 - 96.5 HR15N)
Alumina and Alumina/titania 750 - 1400 HV (91 - 95 HR15N)
WC/Co and WC/CoCr 750 - 1450 HV (91 - 95 HR15N)

Edit: Please see revised hardness info a few posts down.
Reply
12-28-2006, 07:09 PM,
#5
RE: Coating hardness conversion
Gordon Wrote:Hi bhellman



When you can actually do HRC tests on coatings say like a fused NiCrBSi or a thick 13%Cr steel, then at least you can do cross reference tests to see if conversion tables are reasonable or not. With very hard coatings like oxide ceramics and cermets usually HRC tests are not possible. Come to think of it, I wouldn't use HRC for these in the bulk form either. I can remember someone trying to test a sintered tungsten carbide part (~1700 HV) on an HRC machine only to succeed in chipping the diamond indenter and breaking his test part in half.

I have done a lot of work with hard coatings and measuring cross-section microhardness (HV0.3) and HR15N surface hardness (coatings in excess of 0.012" or 300 micrometre thick). From memory I will show roughly the relationship between HV/0.3 and HR15N and the corresponding conversion to HRC. Please note that it is not possible to verify the HRC conversion because the actual HRC test is not viable on these coatings and to be honest think that expressing the hardness for these types of material in HRC is a bit pointless and can be misleading.

Plasma sprayed chromium oxide
1800 HV/0.3 96.5 HR15N (79-80 HRC converted)
1500 HV/0.3 95.5 - 96 HR15N (75-76 HRC converted)

Chromium oxide, alumina and WC/Co
1250 HV/0.3 94.5 - 95 HR15N (71-72 HRC converted)
800 -1000 HV/0.3 92 - 94 HR15N (65-70 HRC converted)

Generally as a rough guide (range relative to grade and quality)
Chromium oxide coatings 1000 - 1800 HV (92 - 96.5 HR15N)
Alumina and Alumina/titania 750 - 1400 HV (91 - 95 HR15N)
WC/Co and WC/CoCr 750 - 1450 HV (91 - 95 HR15N)

Thank you once again Gordon.
This was the best response I've had so far. Without any "offers you can't refuse", is it possible you could extend this list some further. It would help me in my task to modify the program for our ETS+S courses. We are trying to be as up-to-date as ever possible.

br bhe
Reply
12-29-2006, 07:53 PM,
#6
RE: Coating hardness conversion
Hi bhellman

A revised list of coating hardness. Memory obviously not quite so goodRolleyes Hardness values from a few of my old lab reports. The examples may not necessarily be typical of the coating type thoughWink The relationship between cross-sectional microhardness and superficial Rockwell (also effecting conversion to HRC) tends not to be very consistent, particularly between different coating types. Hope this helps.

Plasma sprayed chromium oxide
1800 HV/0.3 96.5 HR15N (79-80 HRC converted)
1500 HV/0.3 95.5 - 96 HR15N (75-76 HRC converted)
1250 HV/0.3 94.5 - 95 HR15N (71-72 HRC converted)

Chromium oxide, alumina, alumina/titania
1000 HV/0.3 92 - 93 HR15N (64-69 HRC converted)
740-1050 HV/0.3 89.5 HR15N
850 HV/1 88 HR15N

HVOF WC/Co, WC/CoCr
700 HV/0.3 86 HR15N (52 HRC converted from HR15N, 60 HRC from HV)
900 HV/0.3 90 HR15N (55-60 HRC claimed in lit.)
900 HV/0.3 - (63-66 HRC claimed in lit.)
1250 HV/0.3 92 .5 HR15N (66-72 HRC converted)

Plasma WC/12Co
780 HV/0.3 87 HR15N (53 HRC converted from HR15N, 63 HRC converted from HV)
1000 HV/0.3 90 HR15N (60 HRC converted from HR15N, 69 HRC converted from HV)

Chromium carbide/25% nickel chromium alloy
990 HV/0.3 89 HR15N (58 HRC converted from HR15N, 69 HRC converted from HV)
750 HV0.3 - (55 HRC claimed in lit. 62 HRC converted from HV)

Generally as a rough guide (range relative to grade and quality)
Chromium oxide coatings 1000 - 1800 HV (92 - 96.5 HR15N)
Alumina and Alumina/titania 750 - 1250 HV (87 - 92 HR15N)
WC/Co and WC/CoCr 750 - 1450 HV (86 - 93 HR15N)
Chromium carbide/NiCr 600 ? 1100 HV (85 ? 90 HR15N)
Reply
01-03-2007, 06:30 PM,
#7
RE: Coating hardness conversion
Image uploaded for Bhellman

[Image: bhellman2.jpg]
Reply
02-18-2020, 10:13 PM,
#8
RE: Coating hardness conversion
(01-03-2007, 06:30 PM)Gordon Wrote: Image uploaded for Bhellman

[Image: bhellman2.jpg]

To Gordon,
I realize this is an old thread...but...
I see the range in which chrome-oxide hardness varies (1000-1800 HV) on the graph. I am stuck below 1300 HV. Can you share how to achieve hardness on the higher scale between 1400-1800 HV

Thankyou,
Neufeld
Reply




Possibly Related Threads…
Thread Author Replies Views Last Post
  Hardness test of the metco 314ns coating sam xu 7 12,129 04-10-2023, 01:59 AM
Last Post: Zhao Yun
Cool Metco FMR unit conversion TintinMilou 5 16,176 07-13-2021, 04:33 PM
Last Post: J!m
  Hardness increase in Chrome Ceramic Plasma Coating DMan 6 2,973 03-25-2021, 01:24 PM
Last Post: DMan
Lightbulb Low hardness on AlTiN Coating Christian93 0 1,456 02-05-2021, 02:32 PM
Last Post: Christian93
  coating hardness using Hipojet 2700M air cooled JRB VIRANI 10 5,658 03-08-2020, 06:41 AM
Last Post: Stephen Booth
  conversion from lpg/propane to hydrogen rmsengineering 0 2,738 12-15-2019, 02:46 PM
Last Post: rmsengineering
  How to increase coating hardness Airbin 2 9,152 11-20-2013, 11:10 AM
Last Post: Airbin
  what's the effect of the spray energy to the coating's hardness? Spark 3 5,819 07-10-2013, 05:55 PM
Last Post: loriolo
Shy flow rate conversion of propane in DJ2700 guang 1 4,934 12-16-2012, 11:52 PM
Last Post: KevGarty
  pencil hardness and tukon hardness test transit 6 19,649 10-04-2012, 02:15 PM
Last Post: bruisjem
  Conversion problem landemarre 3 6,571 12-02-2009, 10:58 AM
Last Post: landemarre
Information Conversion of APS to VPS rayudugirish 1 4,431 08-18-2009, 02:49 PM
Last Post: Gordon
  Hardness Conversion kc77 7 16,743 05-12-2009, 11:37 PM
Last Post: Gordon
  Hardness Testing Methods and Conversion Gordon 3 18,290 04-01-2009, 08:08 PM
Last Post: Gordon
  Coating hardness jimmy 2 7,912 03-24-2008, 10:21 PM
Last Post: hvofhamid



Users browsing this thread: 1 Guest(s)





Surface Engineering Forum Sponsor - Alphatek Hyperformance Coatings Ltd