Un-common surface pattern on coating failure
10-04-2016, 06:09 PM,
#1
Un-common surface pattern on coating failure
Hi All

Never seen this pattern on a roll, coated with W C Co Cr and ground finished

Used in a Non-ferrous Rolling mill, with appx 350 deg C sheet temperature and roll surface temperature of about 100 deg C

Coating was applied using HVOF and ground finished and super polished to 0.1-0.2 microns Ra

Can anyone help with the reason for this pattern on purported coating failure as per the customer?

My best guess was mechanical failure of the part; bearing seizure of roll whilst at work etc...

Thanks in Advance


Shantanu Newar


Attached Files Thumbnail(s)
   
Reply
10-05-2016, 08:39 AM,
#2
RE: Un-common surface pattern on coating failure
(10-04-2016, 06:09 PM)shantanu Wrote: Hi All

Never seen this pattern on a roll, coated with W C Co Cr and ground finished

Used in a Non-ferrous Rolling mill, with appx 350 deg C sheet temperature and roll surface temperature of about 100 deg C

Coating was applied using HVOF and ground finished and super polished to 0.1-0.2 microns Ra

Can anyone help with the reason for this pattern on purported coating failure as per the customer?

My best guess was mechanical failure of the part; bearing seizure of roll whilst at work etc...

Thanks in Advance


Shantanu Newar

Hi Shantanu,
The damage can have mechanical and thermal origin in the combination. 350°C is a critical temperature for WC-Co-Cr coatings on the steel. At this temperature (also locally at the surface) are created in the layer very high tensile stresses which can lead to cracking. The preheating of the roll on 150-200°C before the coating helps to prevent this damage mechanism.
Regards
Vadim
Reply
10-06-2016, 02:55 PM,
#3
RE: Un-common surface pattern on coating failure
Well, 350 deg C is not critical for WCCoCr yet.
And it is the temperature of the sheet, means coating surface temp is much lower.

What I suppose here is a grinding problem.
The coating application itself was great because most of the coating is still there despite a severe damage.
Grinding had overstressed the coating partially during one of the passes, then it has delaminated in service.

Best regards
Vig
Reply




Possibly Related Threads…
Thread Author Replies Views Last Post
Lightning WC10Co4Cr HVOF coating leaves some lumps on the surface tobjung 1 454 10-17-2023, 07:32 AM
Last Post: Vadim Verlotski
  surface speed for HVOF coating process gito 8 5,579 05-03-2019, 01:08 PM
Last Post: Lemster68
  Coating for cyclone internal surface Arturas 0 1,884 12-11-2018, 06:58 AM
Last Post: Arturas
  Remove HVOF Coating in airfoil surface blade achmadarifudinh 5 3,848 07-20-2018, 10:51 AM
Last Post: achmadarifudinh
  Defect Missing Material and Coating Failure achmadarifudinh 2 3,421 02-12-2018, 05:47 AM
Last Post: achmadarifudinh
  Coating surface roughness William 9 26,631 12-26-2017, 10:40 AM
Last Post: Vadim Verlotski
  Powder Coating for Surface Table achmadarifudinh 3 3,752 11-28-2017, 12:19 PM
Last Post: Artyom
  Arc Spray and then Plasma spray? Is this common? cancun555 2 3,091 06-23-2017, 07:11 AM
Last Post: loriolo
  Cr2O3 coating failure specialized 5 5,922 08-23-2016, 02:29 PM
Last Post: specialized
  Gun failure demionkrishan 2 3,980 08-22-2016, 04:49 AM
Last Post: Joris Kraak
  abradable coating failure stvon 11 9,403 11-17-2015, 12:33 PM
Last Post: Joris Kraak
  Boron Carbide as a Surface Coating TCHP222 0 3,760 11-12-2015, 08:06 PM
Last Post: TCHP222
  Metco 450 coating surface problem Yaakov 2 6,724 05-06-2015, 01:54 PM
Last Post: loriolo
  HVOF coating over Induction Hardened surface shantanu 1 3,922 01-30-2015, 08:17 PM
Last Post: djewell
  Coating failure analysis (thermal cycling/abrasion/oxidation) Arkzik 2 5,811 05-28-2013, 07:45 PM
Last Post: Arkzik



Users browsing this thread: 1 Guest(s)





Surface Engineering Forum Sponsor - Alphatek Hyperformance Coatings Ltd