Surface prep issues before APS coating
06-19-2011, 08:09 PM,
#1
Surface prep issues before APS coating
I am trying to grit blast a part to prepare it to be APS coated. When I am finished grit blasting, I check the Rz of the part - it is in spec. However, when I coat the part, the coating sometimes does not adhere. It appears that although the Rz is correct, the surface does not have the correct roughness for the coating to stick. I am using 80 grit aluminum oxide to grit blast, but it appears to break down very quick. Does anyone have any suggestions?
Reply
06-20-2011, 12:08 PM,
#2
RE: Surface prep issues before APS coating
What is the specified roughness? It is possible that you'll have to inform the customer that you need to get more roughness than specified.

It may also be an issue of surface contamination. Have you tested the surfaces for residual oils or greases? Small particles of aluminum oxide can sometimes lodge in the surface of softer metals. Have you ruled this out as a possible issue? You mention the aluminum oxide material seems to be breaking down quickly. Is it possible that residual dust from the oxide is resting on the surface and preventing proper adhesion?

When you say "the coating sometimes does not adhere." are you indicating that there are localized problems on a single piece, or that you are getting proper adhesion on some pieces but not others? It is a minor distinction, but a meaningful one.

If the roughness is in the typical range of what you'd expect for your process, then I would expect this to be a contamination issue of some sort.

Reply
06-20-2011, 12:33 PM,
#3
RE: Surface prep issues before APS coating
The specified roughness is less than 25 um. We have looked at the surface for residue, small particles of aluminum oxide, etc. We have noticed that when the coating does not adhere (and it is almost always in the same place - in a localized, flat area), that the surface resembles more like golf ball dimples than jagged edges - the Rz is the same in either case, but with the golf ball dimples, the coating doesn't adhere. I am curious if changing grit sizes will have an impact?
Reply
06-20-2011, 02:48 PM,
#4
RE: Surface prep issues before APS coating
The specified Rz is less than 25 um, what is your measurement? If your measurement is 20- 24 um will be good for your coating, if it's 10-15 um will be bad for your coating. In aircraft industry, people use 60 grit to do pre-coating preparation, in IGT industry people use 36 grit. Why don't you try the 60 grit to see what happens? Also make sure the part is clean before you blast the part. in another way, maybe you can change the spray pattern will help.
Reply
06-20-2011, 04:23 PM,
#5
RE: Surface prep issues before APS coating
The rounded dimples are no good. That jagged "anchor tooth" profile is always more coducive to good adhesion. It is unusual for aluminum oxide to round off rather than shatter into small pieces and remain jagged. You may have a lower purity oxide that would have a greater tendency to deform.

A few little tricks that may solve the problem would be:

1) If you've been reusing abrasive, then try some virgin material then view under magnification to see if you are getting better (more jagged) profile.

2) Depending on the geometry of the part this area may see an unusal amount of riccochet. If you think that this may be the case try blasting that area of the part last and see if that remedies the problem.

3) Coarser abrasive may help, but may also push you over the roughness limit. I'd also say that derek is accurate in saying that you need to be as close to the 25 um as you can.
Reply
06-20-2011, 05:40 PM,
#6
RE: Surface prep issues before APS coating
80 is too fine for this.
Reply
06-21-2011, 12:56 PM,
#7
RE: Surface prep issues before APS coating
Agree with Derek's opinion. You may try to use 60 grit. By the way, do you coat the part instantly after blasting it?
Reply




Possibly Related Threads…
Thread Author Replies Views Last Post
  Surface prep. with Garnet instead of Al2O3 velocity 1 772 05-14-2019, 04:44 PM
Last Post: Lemster68
  surface speed for HVOF coating process gito 8 1,862 05-03-2019, 01:08 PM
Last Post: Lemster68
  Coating for cyclone internal surface Arturas 0 728 12-11-2018, 06:58 AM
Last Post: Arturas
  Coating surface roughness William 9 20,631 12-26-2017, 10:40 AM
Last Post: Vadim Verlotski
  Powder Coating for Surface Table achmadarifudinh 3 1,944 11-28-2017, 12:19 PM
Last Post: Artyom
  Un-common surface pattern on coating failure shantanu 2 2,110 10-06-2016, 02:55 PM
Last Post: Vig
  Boron Carbide as a Surface Coating TCHP222 0 2,324 11-12-2015, 08:06 PM
Last Post: TCHP222
  Metco 450 coating surface problem Yaakov 2 4,398 05-06-2015, 01:54 PM
Last Post: loriolo
  HVOF coating over Induction Hardened surface shantanu 1 2,648 01-30-2015, 08:17 PM
Last Post: djewell
  Issues in Al coating on photoresist xoobiii 5 3,856 03-13-2012, 10:26 AM
Last Post: loriolo
  Surface Speeds and traverse for coating Cro-167 js2know 2 3,569 12-23-2011, 02:15 PM
Last Post: Gordon
  Inconel 625 coating on flange surface gops123 5 10,900 04-05-2011, 01:54 PM
Last Post: Stuart Milton
  Erosion-corrosion issues in boiler applications sivakumar 1 5,092 05-04-2010, 08:40 PM
Last Post: MichiganMan
  Build up and low flame issues! TurbineRepair 4 5,194 09-02-2008, 01:06 PM
Last Post: erick212
  Porous Machined Surface on Part Lower Inner Diameter on Inco 718 Coating Surface Alexangel1226 4 7,020 03-19-2008, 02:05 PM
Last Post: Gordon



Users browsing this thread: 1 Guest(s)





Surface Engineering Forum Sponsor - Alphatek Hyperformance Coatings Ltd