Electro Spark Surface Deposition Machine
09-10-2014, 07:20 PM,
#1
Electro Spark Surface Deposition Machine
   

Hi,

We are working on feed crushing blade coating. We applied hot coating WC/Co+NiCrBSi %50 but not get enough service life. I saw some brazing application and an electro spark surface coating machine.

It's name is Rocklinizer. It works on 3 different electrode. TitaniumCarbide, TungstenCarbide.

Is any body try to use this machine?


Is any body know the bonding strength ?


What is the correct application this like surface parts? (Feed crushing blade, crushing hammer, farming blades ect)


I check some doc. about this machine. I thing may be work well on this like application.

Thanks for your reply.
Reply
09-11-2014, 06:38 PM,
#2
RE: Electro Spark Surface Deposition Machine
My experience with electrospark deposition is that it is extremely slow and applies a very thin layer of tungsten carbide on the part. I have never seen bond strength data. It would probably take you a week to coat your crusher parts with this machine.

Why did you choose the WC/Co-50NiCrBSi coating material? An 86WC10Co4Cr coating would provide better wear protection because it has a much higher carbide concentration.
Reply
09-12-2014, 05:43 PM,
#3
RE: Electro Spark Surface Deposition Machine
(09-10-2014, 07:20 PM)Met.Eng. Wrote: Hi,

We are working on feed crushing blade coating. We applied hot coating WC/Co+NiCrBSi %50 but not get enough service life. I saw some brazing application and an electro spark surface coating machine.

It's name is Rocklinizer. It works on 3 different electrode. TitaniumCarbide, TungstenCarbide.

Is any body try to use this machine?


Is any body know the bonding strength ?


What is the correct application this like surface parts? (Feed crushing blade, crushing hammer, farming blades ect)


I check some doc. about this machine. I thing may be work well on this like application.

Thanks for your reply.

Hi,

You can see here:

https://plasmajet.ro/en/electro-spark-deposition/

Ion
Reply




Possibly Related Threads…
Thread Author Replies Views Last Post
  Electron-beam physical vapor deposition masking jtonic77 6 3,221 10-04-2022, 06:31 PM
Last Post: SakshiVerma
  Spark Issue on DJ2600 HVOF Flame xxxxmgulkokan 3 2,135 08-31-2022, 03:15 PM
Last Post: Red Baron
  The conditions of deposition of CoNiCrAl+Si at the HVOF Serg 0 1,750 09-20-2018, 07:37 AM
Last Post: Serg
  Effect of weather on deposition efficiency Max K 3 5,582 08-06-2013, 04:40 PM
Last Post: GMA thermal spray systems
  Molybdenum deposition on copper plasmajet1990 9 8,836 06-04-2013, 09:07 PM
Last Post: plasmajet1990
  Better deposition without changing parameters and feedrate? Pnewbie 5 7,968 02-03-2012, 01:16 AM
Last Post: LEN WOOD
  Measuring deposition efficiency and check the microstructures of the coatings??????? fahad03092 7 10,457 10-25-2011, 02:05 PM
Last Post: djewell
  Deposition effect of Metco 42C Met.Eng. 5 9,468 08-11-2011, 03:10 AM
Last Post: Gordon
Question obstruction during deposition of amorphous powders desMoira 6 7,344 07-22-2010, 01:18 PM
Last Post: desMoira
  Deposition efficiency of Metco 131VF raviswanadha 3 8,006 03-28-2009, 02:52 PM
Last Post: Gordon
  Deposition Efficiency Measurement deepskysea 3 8,872 09-05-2008, 02:38 PM
Last Post: Gordon
  Porous Machined Surface on Part Lower Inner Diameter on Inco 718 Coating Surface Alexangel1226 4 8,980 03-19-2008, 02:05 PM
Last Post: Gordon



Users browsing this thread: 1 Guest(s)





Surface Engineering Forum Sponsor - Alphatek Hyperformance Coatings Ltd