Posted by Giuseppe (22.214.171.124) on 12:02:50 14/01/05
In Reply to:Re: VICKERS HARDNESS HV10 VS HV30 posted by Gordon England
: :I'm looking for experimental data and/or correlation formula to compare 130 HV30, 135 HV30, 140 HV experimental data to the required HV10 customer request.
: : As per my understanding (some reference to BS 860:1967 / ISO 18265:2003) HV10/HV30 are equivalent.
: : Data are referred to:
: : - ASTM A216 WCB
: : - Weld repair
: : - base material 130-140
: : - H.A.Z. 131-138
: : - Heat treatment, PWHT 910°C..
: : Thank you in advance.
: HV/10 and HV/30 results are equivalent in that they use the same scale. In practice though, there can be small differences in the results obtained, which is mainly dependent on the particular test specimens material and nature. This is why it is important for stating the test conditions as in HV/10 against just HV or VPN.
: A specification stating a hardness in say HV/10 should only be validated using that same test. It is not good practice to use another method and convert the result.
: Regards Gordon
Nature of Thermal Spray Coatings
Surface Engineering in a Nutshell
Surface Engineering Forum
Thermal Spray Gun Repair Service
Plasma Consumable Parts
Thermal Spray Powder Supplies
Thermal Spray Coatings on Carbon and Glass Fibre Reinforced Polymers
HVOF Coating of Paper Making Roll
Thermal Spray Processes:
Combustion Wire Thermal Spray Process
Combustion Powder Thermal Spray Process
Arc Wire Thermal Spray Process
Plasma Thermal Spray Process
HVOF Thermal Spray Process
HVAF Thermal Spray Process
Detonation Thermal Spray Process
Plasma Flame Theory
Cold Spray Coating Process
Wear and Use of Thermal Spray Coatings
Corrosion and Use of Thermal Spray Coatings
Glossary of Thermal Spray and Surface Engineering Terms
Image Directory for Thermal Spray Coatings
Plasma Gas Flow Information
Plasma Gas Flow Correction Calculator
Links to other interesting sites related to thermal spray and surface engineering
Periodic Table of the Elements
Calculators for Conversion between Units of Measurement
Surface Engineering Message Board Archive
Surface Engineering Message Board Archive Index
© Copyright Gordon England