WC-Co by HVOF on Monel Ball valve
10-04-2012, 10:50 AM,
#1
WC-Co by HVOF on Monel Ball valve
Hi all,
I need your suggestions and solution to the problem we are facing.
We have WC-Co by HVOF on Monel Ball valve to work in "Ammonium Bifluoride with excess Hydrogen Fluoride" media. The customer has complained that the coating is wearing faster. A brief description is given below
Service Temp - 285F
Pressure - 3 to 5 psig.
Media - Ammonium Bifluoride with excess Hydrogen Fluoride
Min/max on temperatures - Ambient to 285F
Flow rate - <1/2 GPM
Required shut off - Class VI
Cycles per day - 24
Ball Valve, Size 25mm Class 800, Full bore, Seat they are using right now is Glass filled PTFE.
Can you suggest what could be the problem And also any alternate material to be sprayed on this.
regards
Reply
10-09-2012, 06:15 PM,
#2
RE: WC-Co by HVOF on Monel Ball valve
Hi,

Your issue is cobalt matrix, for example, Ammonium bifluoride in addition with some acid is use to extract cobalt from certain kind of soil in mining industry.

Simply switch your matrix to a Ni/Cr Matrix.

Regards
Reply
10-10-2012, 01:25 PM,
#3
RE: WC-Co by HVOF on Monel Ball valve
(10-09-2012, 06:15 PM)Spraytube Wrote: Hi,

Your issue is cobalt matrix, for example, Ammonium bifluoride in addition with some acid is use to extract cobalt from certain kind of soil in mining industry.

Simply switch your matrix to a Ni/Cr Matrix.

Regards

Hi thanks for your post. so you suggest we us Tungsten carbide with Nickel binder instead of cobalt binder?
regards
Reply
10-10-2012, 05:59 PM,
#4
RE: WC-Co by HVOF on Monel Ball valve
Hi,

Sorry my explanation wasn't clear enough.
I was thinking about a WC 10Ni 5Cr.

Using Ni/Cr binder will helps to have a better resistance to corrosion.
With this kind of powder you will have a higher hardness than WC/Ni coating (consequence of the hardening effect of the chromium in the binder) but the toughness will be reduced...

Regards



Reply
10-15-2012, 12:03 PM,
#5
RE: WC-Co by HVOF on Monel Ball valve
Thank you very much for your valuable suggestion we will try with that composition and will post back the result
regards
Reply




Possibly Related Threads…
Thread Author Replies Views Last Post
Pencil Ball Mill Shaft- Journal Bearing Area HVOF Coating Issue tobjung 0 745 02-02-2023, 06:44 PM
Last Post: tobjung
  sealing gate valve WC coated problem ehsan 16 17,443 06-27-2022, 12:27 PM
Last Post: sushil1405
  Valve seat coating shantanu 2 4,181 02-19-2015, 03:23 AM
Last Post: Axis Machine
  Hard coating on valve Edson 3 5,064 02-19-2015, 03:18 AM
Last Post: Axis Machine
  ball valve and gate valve coating Jaydev 2 5,708 01-29-2015, 05:06 PM
Last Post: IgorGarcia
  JP-8000 w/ Monel 400? gpdm 3 5,247 02-07-2014, 04:41 PM
Last Post: gpdm
  Tungsten Carbide HVOF Coated Ball Valves grinding and Lapping constraints --- Reg sreenuvundela 4 11,402 07-29-2013, 09:04 AM
Last Post: Met.Eng.
  After ball milling, is the powder particle size will be changed? fahad03092 1 4,590 11-21-2012, 11:14 PM
Last Post: loriolo
  substrate deformation of WC coating in gate valve ehsan 2 5,982 12-14-2010, 09:15 AM
Last Post: Asiaf
  Thickness Measurement of Sprayed Monel wrjordan 15 17,570 11-08-2009, 05:40 AM
Last Post: k09
  valve opening procedure sutech 7 10,041 11-12-2008, 05:46 AM
Last Post: Intel55
  twin wire arc spraying equipment for stainless steel wire, monel wire, etc. technovel 6 12,770 08-01-2008, 11:59 AM
Last Post: adam wintle



Users browsing this thread: 1 Guest(s)





Surface Engineering Forum Sponsor - Alphatek Hyperformance Coatings Ltd