Thermal barrier delamination problem
08-31-2015, 07:34 PM,
#1
Thermal barrier delamination problem
Dear experts,

I have a delamination problem in the thermal barrier coating of a plaque who is exposed to 950 C. I used Nicroloy like bond coat (0.004 in) and Ytrria Zirconia (0.012 in) We used the Plasma 7MC equipment with the next parameters:
Hydrogen Pressure/ 70 psi
Hydrogen flow/ 15 SCFH
Argon pressure/ 100 psi
Argon flow/ 100 SCFH
Amp./ 500 Amp.
Vol./ 70 V
Standoff D./ 6 in
Feed rate 30 gr/min
Sustrate/ 310SS

I made some test with mild steel substrate using 1000 C and no delamination occured, so I dont know what happen, Do you have any idea about this problem?? what can be the wrong thing??

Thank you very much

Hector Monjardin


Attached Files Thumbnail(s)
   
Reply
09-01-2015, 10:11 AM, (This post was last modified: 09-01-2015, 11:44 AM by Vadim Verlotski.)
#2
RE: Thermal barrier delamination problem
Hi Hector,

There are two important conditions for the functioning of thermal barrier coatings at temperatures above 900°C:

1. Basic material has a nickel-based alloy (Inconel or Nimonic).
2. Bond coat must consist of MCrAlY alloy (better NiCoCrReAlY alloy).

All other base materials and bond coats can not be used at temperatures above 800°C due oxidation of the bond coats and diffusion between the substrate and bond coat. Oxidation and spalling of the bond coat can be clearly seen on the image.

Regards

Vadim
Reply
09-25-2015, 11:05 AM,
#3
RE: Thermal barrier delamination problem
Hi Hector,

The base material is a 310SS that should not be a problem right, it should suitable for these higher temperatures?

Maybe bondcoating too porous?

regards,
Joris


Reply




Possibly Related Threads…
Thread Author Replies Views Last Post
  Yellow Spot on Thermal Barrier Coating achmadarifudinh 11 4,836 11-30-2020, 05:32 PM
Last Post: Lemster68
  T800 coating delamination alvliew 5 5,672 05-05-2017, 02:54 AM
Last Post: KevinS
  Coating delamination problem texnicar 13 11,515 07-07-2015, 10:37 PM
Last Post: Johnny_Blaze
  45VFNS Delamination Meeker77 2 4,161 05-24-2015, 05:46 PM
Last Post: Meeker77
  Thermal Barrier Coating Aluminum Substrate for corrosion resistance alaskangrown 4 6,573 03-02-2015, 06:43 PM
Last Post: alaskangrown
  Delamination in the bond coat sprayed on a Ti specimen Justin 9 10,190 01-06-2014, 10:00 PM
Last Post: KevinS
  Delamination BatuhanCemreAyas 2 4,237 01-02-2014, 06:30 AM
Last Post: sprayjet
  delamination in the coating codep 3 7,059 05-15-2013, 05:04 PM
Last Post: Gordon
  High velocity thermal barrier coating djewell 2 5,165 09-04-2012, 07:50 PM
Last Post: farzin_g1
  delamination in general epilson 1 4,168 06-21-2011, 07:45 PM
Last Post: Gordon
  Thermal bridging problem AllyG 2 7,400 12-20-2010, 06:10 PM
Last Post: AllyG
Cool Instrument to check coating thickness of Thermal Barrier Coatings odski0317 5 17,687 12-01-2010, 10:09 AM
Last Post: dienngothe
  APS WC coating delamination brianf121 2 5,466 07-22-2010, 04:30 PM
Last Post: brianf121
  About Thermal Barrier Coating Porosity Amanda 3 9,574 04-10-2009, 03:34 PM
Last Post: Gordon
  delamination of spray - fuse coating Arturas 10 12,934 04-01-2009, 05:13 PM
Last Post: Gordon



Users browsing this thread: 1 Guest(s)





Surface Engineering Forum Sponsor - Alphatek Hyperformance Coatings Ltd