Heat treatment after HVOF process to decrease porosity
05-18-2015, 06:16 AM,
#1
Heat treatment after HVOF process to decrease porosity
Hello,

I come from Viet Nam where the thermal spray technology still new. In our workshop, we have wire arc spray (from TAFA) and HVOF system (from Castolin).

I have problem with my customer, they need WC - Niken coating sprayed by HVOF using in corrosion environment. So that, they need the porosity of surface coating is minimum and they suggest us heat treatment (fusing) after spray to decrease porosity.

We do not have the experience in this case. What is temperature for heat treatment? time, enviroment heat treatment?

So please help us if you have experience is this case.

Thanks and best regards
Reply
05-18-2015, 10:15 AM,
#2
RE: Heat treatment after HVOF process to decrease porosity
(05-18-2015, 06:16 AM)Giroud Wrote: Hello,

I come from Viet Nam where the thermal spray technology still new. In our workshop, we have wire arc spray (from TAFA) and HVOF system (from Castolin).

I have problem with my customer, they need WC - Niken coating sprayed by HVOF using in corrosion environment. So that, they need the porosity of surface coating is minimum and they suggest us heat treatment (fusing) after spray to decrease porosity.

We do not have the experience in this case. What is temperature for heat treatment? time, enviroment heat treatment?

So please help us if you have experience is this case.

Thanks and best regards

Hi Giroud,
Fuse undergo only a coatings of self-fluxing alloys such NiCrBSi or CoCrBSi. There are NiCrBSi alloy powders with the addition of WC, which can also to be fused. For coatings of NiCrBSi self-fluxing alloys applied usually simple flame spraying, and then melt at 1050°C. Fuse may be performed with burners or with inductor, but also in the furnace with a protective atmosphere.
If you mean HVOF-coatings of WC-Co or WC-Co-Cr, it is impossible to melt them.
Reply
06-09-2015, 06:44 AM,
#3
RE: Heat treatment after HVOF process to decrease porosity
(05-18-2015, 06:16 AM)Giroud Wrote: Hello,

I come from Viet Nam where the thermal spray technology still new. In our workshop, we have wire arc spray (from TAFA) and HVOF system (from Castolin).

I have problem with my customer, they need WC - Niken coating sprayed by HVOF using in corrosion environment. So that, they need the porosity of surface coating is minimum and they suggest us heat treatment (fusing) after spray to decrease porosity.

We do not have the experience in this case. What is temperature for heat treatment? time, enviroment heat treatment?

So please help us if you have experience is this case.

Thanks and best regards

Hello
Mr.Vadim Verlotski said You quite rightly on the need to apply a coating of self-fluxing :type NiCrBSi.The one thing I disagree with him. Perfectly self-fluxing coatings are applied by HVOF up to a thickness of 2.5-2.7 mm and have a porosity of practically "0".Apply melting is not necessary
Thermal spray method is not so new in Vietnam. Our equipment HVOF Termika-3 and FS Termika-2 is already working in your country for 4 years.

Reply
07-13-2015, 05:51 AM,
#4
RE: Heat treatment after HVOF process to decrease porosity
(05-18-2015, 06:16 AM)Giroud Wrote: Hello,

I come from Viet Nam where the thermal spray technology still new. In our workshop, we have wire arc spray (from TAFA) and HVOF system (from Castolin).

I have problem with my customer, they need WC - Niken coating sprayed by HVOF using in corrosion environment. So that, they need the porosity of surface coating is minimum and they suggest us heat treatment (fusing) after spray to decrease porosity.

We do not have the experience in this case. What is temperature for heat treatment? time, enviroment heat treatment?

So please help us if you have experience is this case.

Thanks and best regards

Reply




Possibly Related Threads…
Thread Author Replies Views Last Post
  Surface Treatment of Ceramic Coatings brkozdemir41 0 1,922 12-18-2020, 12:09 AM
Last Post: brkozdemir41
  Porosity problem - HVOF thaisrms 6 4,915 08-28-2020, 06:52 AM
Last Post: Vadim Verlotski
  Request for solution to reduce porosity in HVOF Tungsten Carbide Coatings sreenuvundela 7 12,266 07-22-2020, 08:01 AM
Last Post: Simon Kim
  surface speed for HVOF coating process gito 8 5,548 05-03-2019, 01:08 PM
Last Post: Lemster68
  heat treatment of MCrAlY coatings clover 4 8,078 06-26-2017, 12:55 PM
Last Post: Nesher
  Fusing and heat treatment sprayloud 3 3,261 06-24-2017, 12:30 PM
Last Post: Vadim Verlotski
  Coating and Heat treatment Improvements demionkrishan 2 2,845 04-22-2017, 06:13 AM
Last Post: demionkrishan
  HVOF porosity sprayloud 4 6,042 11-28-2016, 02:27 PM
Last Post: MVagusta
  Poor flame with Ni-based metallic powder - HVOF process Roy 2 4,592 02-26-2016, 12:30 AM
Last Post: Roy
  Masking tape for high-heat ceramic coating. texnicar 1 4,119 04-21-2015, 04:09 PM
Last Post: cris1904
  Sprayed, welded or cast alloys for high heat Zanitech 2 4,038 10-01-2013, 09:08 PM
Last Post: Met.Eng.
  Process Gasses Purity Impact towards Plasma Spray Process, equipment or outcome Alexangel1226 8 12,283 06-12-2012, 02:46 PM
Last Post: Eric Tolliver
  How to decrease interface contamination Zhiguo 2 5,623 02-24-2012, 07:04 AM
Last Post: Zhiguo
  How to decrease the bigger voids of Ni-18.5Cr-6Al coating? Justin 3 4,416 12-17-2011, 03:41 AM
Last Post: Gordon
  oxide stringers and porosity In HVOF WC-CO wilfred1963 13 13,876 03-22-2011, 07:45 AM
Last Post: Khairul Anwar



Users browsing this thread: 1 Guest(s)





Surface Engineering Forum Sponsor - Alphatek Hyperformance Coatings Ltd