: : I have a problem with the interface of Amdry 962/substrate it appers a line of oxidation we already change the alumimun oxide but the problem is the same . How can I solve this problem.
:
: can you explain moor
Hi Patricia
I assume you are referring to interface contamination from imbedded or retained particles from the grit blasting process. You will need to experiment with different blasting pressures, stand off distances, angles and blasting media size and type.