Posted by Gordon England (62.252.0.5) on 16:29:18 18/11/04
In Reply to:Re: Flaws in stellite coatings posted by Paul Burkhardt
: The process used is Plasma spray not plasma transfer which I understand relies on fusion with the base metal. At the moment I believe that the coatings we have tried to machine are too thick. The pre-coat m/c drawing calls up sizes for stellite welding not plasma spray and I would guess that 5mm allowance would be too thick. Am I heading in the right direction?
Hi Paul
Yes, I think you are. I'm not sure what the recommended thickness limit would be for your particular coating, but typically, a coarse cobalt alloy would be limited around to 1 - 2 mm. Very fine powders would be very much lower at around 0.4 mm. This could well be causing your problems or at least contributing to them.
Regards Gordon
Follow Ups:
Please go to the new Surface Engineering Forum as this old message board is a read only archive. Please copy and paste relevant information or link to the page if you wish to reactivate a thread on the new forum.
Introducing
Nature of Thermal Spray Coatings
Surface Engineering in a Nutshell
Surface Engineering Forum
Thermal Spray Gun Repair Service
Plasma Consumable Parts
Thermal Spray Powder Supplies
Applications:
Thermal Spray Coatings on Carbon and Glass Fibre Reinforced Polymers
HVOF Coating of Paper Making Roll
Abradable Coatings
Thermal Spray Processes:
Combustion Wire Thermal Spray Process
Combustion Powder Thermal Spray Process
Arc Wire Thermal Spray Process
Plasma Thermal Spray Process
HVOF Thermal Spray Process
HVAF Thermal Spray Process
Detonation Thermal Spray Process
Plasma Flame Theory
Cold Spray Coating Process
Wear and Use of Thermal Spray Coatings
Corrosion and Use of Thermal Spray Coatings
Glossary of Thermal Spray and Surface Engineering Terms
Image Directory for Thermal Spray Coatings
Plasma Gas Flow Information
Plasma Gas Flow Correction Calculator
Contact Form
Links to other interesting sites related to thermal spray and surface engineering
Reciprocal Links
Periodic Table of the Elements
SI Units
Calculators for Conversion between Units of Measurement
Hardness Testing
Surface Engineering Message Board Archive
Surface Engineering Message Board Archive Index
Photography Gallery2
Photography Gallery3
© Copyright Gordon England