Posted by Gordon England (62.252.0.12) on 11:36:27 19/06/06
In Reply to: Hardening Stainless Steel posted by Peter
Hi Peter
Oil or air quench from a temperature of 950/1020 degree C, then
temper at a suitable temperature to achieve hardness required. If
you are using very rapid heating methods like induction then higher
hardening temperatures may be needed.
Regards Gordon