Posted by Bill Ferree on January 21, 2004 at 16:43:35:
In Reply to: Re: tungsten carbide (nickel based) coating posted by Gordon England on February 13, 2003 at 11:11:45:
: : Does anyone out there know a suitable coefficient of friction (static or dynamic) for a valve seat ring coated with a nickel based tungston carbide rubbing against a cast nickel-copper wedge? (This is a wedge gate valve in steam or seawater)
: : I'd appreciate your input.
: : Ken
: Hi Ken
: I doubt whether you will get any specific values for this combination without testing it for yourself. I would suspect the coefficient of friction will be not be particularly low. Are you experiencing problems with this combination of materials?
: Regards Gordon