Posted by John Carleton on August 27, 2003 at 10:04:26:

Hi Gordon/all,

How good do you think HVOF nickel chrome carbide would be against 400 C TiCl4 gas (Ticle). The reason I ask is that a recent trial appears to have washed away the coating. I'm now thinking of the Hvof tungsten bonded in nickel

Many thanks for your help

John

Follow Ups: